首页 > 产品展示 > 晶体
晶体
晶体
PARAMETER

1.双折射晶体

物理&光学性质

透光范围

500-4000nm

350-2300nm

190-3500nm

晶体结构

Trigonal

Trigonal,

Trigonal,Space Group R3c

晶系

Positive Uniaxial

Positive Uniaxial

Negative Uniaxial

含晶细胞

a=b=7.12 A,c=6.29 A

a=6.37 A

a=b=12.532 A,c=12.717 A

密度

4.22g/cm3

2.7g/cm3

3.85g/cm3

潮解性

High

Low

Low

莫氏硬度

5

 

3

4.5

热膨胀系数

aa=4.43*10﹣6/k

ac=11.37*10﹣6/k

aa=24.39*10﹣5/k

ac=5.68*10﹣5/k

Aa=4*10﹣6/k

Ac=36*10﹣6/k

光学均匀性

10﹣6/cm

10﹣6/cm

10﹣6/cm

吸收系数

 

<0.1%@1064nm< p="">

 

<0.1%@1064nm< p="">

<0.1%@1064nm< p="">

在45°时屈光指数,双折射,离散角(ρ)

ne=2.2154,No=1.9929

l n=0.2251

ρ=6.042°@633nm

ne=1.48520,no=1.6557

l n=0.1705

ρ=6.20°@633nm

ne=1.54381,no=1.67056

l n=0.1222

ρ=4.345°@532nm

特性

直径

Max.30-40mm

Max.150mm

Max.40-50mm

长度

Max.25-35mm

Max.100mm

Max.25-35mm

光洁度

Better than 20/10 Scratch/Dig Per MIL-0-13830A

光束偏移

<10arc seconds

光轴方向

+/-0.2°

面形

<λ/8@633nm

透过波前畸变

<λ/4@633nm

镀膜

Upon Specification

 

2. 双折射晶体

 物理&光学性质

透光范围

420-5200nm

120-8500nm

200-2300nm

晶体结构

Trigonal,SpaceGroup R3c

Trigonal,SpaceGroup R3c

Trigonal,SpaceGroup R3c

晶系

Positive Uniaxial

Positive Uniaxial

Negative Uniaxial

含晶细胞

a=b=0.515 A,c=13.863 A

a=b=4.621 A,c=3.053 A


密度

4.64g/cm3

3.18g/cm3

2.65g/cm3

潮解性

Low

Low

Low

莫氏硬度

5

 

6

7

热膨胀系数

Aa=2.0*10﹣6/k@25℃

Ac=2.2*10﹣6/k@25℃

 

Aa=6.23-9.25*10﹣6/k

Ac=10.86-14.54*10﹣6/k

Aa=6.2*10﹣6/k

Ac=10.7*10﹣6/k

光学均匀性

5*10﹣5/cm

10﹣6/cm

10﹣6/cm

吸收系数

0.1%/cm﹣1@1064nm

0.07at 0.2um;0.02 at 5.0um

0.02@500nm

0.1%/cm﹣1@1064nm

在45°时屈光指数,双折射,离散角(ρ)

Ne=2.20263,No=2.28629

△ n=0.08366

ρ=2.135°@633nm

Ne=1.38876,No=1.37698

△ n=0.01178

ρ=0.488°@633nm

Ne=1.55170,No=1.54265

△ n=0.00905

ρ=0.335°@532nm

特性

直径

Max.30-40mm

Max.50mm

Max.100mm

长度

Max.25-35mm

Max.100mm

Max.100mm

光洁度

Better than 20/10 Scratch/Dig Per MIL-0-13830A

光束偏离

<10arc seconds

光轴方向

+/-0.2°

面形

<λ/8@633nm

透过波前畸变

<λ/4@633nm

镀膜

Upon Specification


3.激光晶体

物理&光学性质

化学分子

420-5200nm

120-8500nm

200-2300nm

晶体结构

Trigonal,Space Group R3c

Trigonal,Space Group R3c

Trigonal,Space Group R3c

熔点

Positive Uniaxial

Positive Uniaxial

Negative Uniaxial

密度

a=5.14A

a=b=4.621 A,c=3.053 A


莫氏硬度

4.64g/cm3

3.18g/cm3

2.65g/cm3

潮解性

Low

Low

Low

热传导系数

5

 

6

7

热膨胀系数

aa=2.0*10﹣6/k@25℃

ac=2.2*10﹣6/k@25℃

 

aa=6.23-9.25*10﹣6/k

ac=10.86-14.54*10﹣6/k

aa=6.2*10﹣6/k

ac=10.7*10﹣6/k

激射波长

5*10﹣5/cm

10﹣6/cm

10﹣6/cm

吸收范围

<0.1%/cm@1064nm

0.07at 0.2um;0.02 at 5.0um

 

<0.1%/cm@1064nm

晶格常数

ne=2.20263,no=2.28629

l n=0.08366

ρ=2.135°@633nm

ne=1.38876,No=1.37698

l n=0.01178

ρ=0.488°@633nm

ne=1.55170,No=1.54265

l n=0.00905

ρ=0.335°@532nm

荧光寿命

420-5200nm

120-8500nm

200-2300nm

吸收系数

Trigonal,Space Group R3c

Trigonal,Space Group R3c

Trigonal,Space Group R3c

折射率

Positive Uniaxial

Positive Uniaxial

Negative Uniaxial

极化发射

a=5.14A

a=b=4.621 A,c=3.053 A


特性

内容

0.06-0.5 wt%Ti dopant

0.5-1.2 atm%Nd dopant(10% tolerance)

0.2-3 atm%Nd dopant(10% tolerance)

品质因数

100-300



孔径

2-50mm

3-14mm

1-20mm

路径长度

2-130mm

1-60mm

0.02-20mm

结束配置

Flat/Flat or Brewster/Brewster Ends or Specified

 

4.激光晶体

晶体

Ti:Sapphire

Nd:YAG

      Nd:YVO4

晶向

Optical Axis C Normal to Rod Axis

<111>Crystalline Direction(+/-0.5℃)

a-cut Crystalline Direction(+/-0.5℃)

平行度

<10 arc seconds

光洁度

Better than 60/40 Scratch/Dig

Per MIL-O-13830A

Better than 20/10 Scratch/Dig

Per MIL-O-13830A

Better than 20/10Scratch/Dig

Per MIL-O-13830A

面形

<λ/10@633nm

<λ/10@632.8nm

<λ/10@632.8nm

透过波前

<λ/4 per inch@633nm

<λ/10 @632.8nm for3-7mm

<λ/8 per inch@632.8nm for>=7mm

<λ/8@633nm

垂直度

<5 arc minutes

<5 arc minutes

<5 arc minutes

通光口径

Central 90%

 

Central 95%

 

Central 95%

 

倒角

0.15*44°

 

0.15*45°

 

0.15*45°

损伤阀值

Over 15J/cm2(Rods without Coating) over 700MW/cm2(Coating)

Over 15J/cm2(Rods without Coating) over 700MW/cm2(Coating)

Over 15J/cm2(Rods without Coating) over 700MW/cm2(Coating)

镀膜







AR@700-1100nm

a)AR@10664nm,R<0.1%< p="">

a)AR@10664nm,R<0.1%< p="">

b)AR@1064nm,R<0.1%;ht@808nm,t>95%

b)AR@1064nm,R<0.1%;ht@808nm< p="">

,t>95%

c)HR@1064nm,R<99.8%;ht@808nm,t>95%

c)HR@1064nm,R<99.8%;ht@808nm< p="">

,t>95%

d)HR@1064nm,R<99.8%;ht@808nm,< p="">

t>95%;HR@532nm,R>99%

d)HR@1064nm,R<99.8%;ht@808nm< p="">

,t>95%;HR@532nm,R>99%

5.非线性光学聚合物晶体

物理&光学性质

晶体结构

Tigonal,Space Group R3c

Otthorhombic,Point Group mm^2

Otthorhombic,Point Group mm^2

Tigonal,Space Group R3c

透过范围

189-3500nm

350-4500nm

160-2600nm

420-5200nm

含晶细胞

A=b=12.532 A

C=12.717 A

A=6.404 A

B=10.616 A

C=12.814 A

A=8.44731A

B=7.3788 A

C=5.1395 A

a=0.515A

c=13.863A

熔点

1095+/-5℃

1172℃ Incongruent

834℃

1255+/-5℃

居里温度

925+/-5℃

936℃

5

1140+/-5℃

光学均匀性

△n=10-6/cm

△n=10-6/cm

△n=10-6/cm

△n=5*10-5/cm

莫氏硬度

4.5

 

5

6

5

密度

3.85g/cm^3

 

3.01g/cm^3

 

2.47g/cm^3

 

4.64g/cm^3

 

热导系数

^C,0.012W/m/k

‖C,0.016W/m/k 

 

0.03 W/m/k

 

0.035 W/m/k

 

0.046 W/m/k

 

二倍频波长范围

205-1750nm

1000-2000nm

800-2000nm

1100-3000nm

吸收系数

<0.1%/cm@1064nm

<1%/cm@1064nm and 532nm

<=1%/cm@1064nm

<0.1%/cm@1064nm

非线性光学 系数

d21=2.2pm/V

d31=0.08pm/V

d22=2.2pm/V

d31=1.95pm/V

d32=3.90pm/V

d33=15.3pm/V

d24=3.90pm/V

d15=1.95pm/V

 

d21=0.67pm/V

d22=0.04pm/V

d23=0.85pm/V

d34=0.85pm/V

d16=0.67pm/V

 

d21=d22=d16=2.6pm/V

d31=d32=d24=4.6pm/V

d33=25.6 pm/V

损伤阀值@1064nm

12.9J/cm^2 9.9GW/ cm^2

6.0J/cm^2 4.6GW/ cm^2

24.6J/cm^2 18.9GW/ cm^2

200GW/ cm^2

折射率@1064nm@532nm

Ne=1.5425

No=1.6551

Ne=1.5555

No=1.6749

 

Nx=1.73991

Ny=1.74802

Nz=1.82956

Nx=1.77903

Ny=1.79002

Nz=1.88628

 

Nx=1.56447

Ny=1.59050

Nz=1.60538

Nx=1.57842

Ny=1.60650

Nz=1.62154

Ne=2.23216

No=2.15600

Ne=2.32309

No=2.23415

 

6.非线性光学聚合物晶体

标准规格和功能

NLO Crystal

BBO

KTP

LBO

LiNbO3

角度公差

△θ<+/-0.5°;△o<+/-0.5

尺寸公差

(w+/-0.1mm)*(H+/-0.1mm)*(L+0.2mm/-0.1mm)

(w+/-0.1mm)*(H+/-0.1mm)*(L+0.2mm/-0.1mm)

(w+/-0.1mm)*(H+/-0.2mm)*(L+0.2mm/-0.2mm)

(w+/-0.1mm)*(H+/-0.2mm)*(L+0.2mm/-0.2mm)

面形

<λ/8@633nm

 

<λ/8@633nm

 

<λ/4@632.8nm

 

<λ/8@633nm

 

光洁度

Better than 10/5 Scratch /Dig per MIL-O-13830A

平行度

<20 arc seconds

垂直度

<5 arc minutes

 

<5 arc minutes

 

<30 arc minutes

 

<5 arc minutes

 

透过波前

<λ/8@633nm

 

<λ/8@633nm

 

<λ/4@632nm

 

<λ/8@633nm

 

通光口径

>90% Central Area

 

>90% Central Area

 

>80% Central Area

 

>90% Central Area

 

孔径

1*1-12*12mm

1*1-10*10mm

2-10mm

1-50mm

长度

0.02-25mm

0.05-20mm

0.3-20mm

0.3-20mm

相匹配类型

TypeⅠor TypeⅡ

TypeⅡ

TypeⅠor TypeⅡ

TypeⅠor TypeⅡ

端面形式

Flat or Brewster or Specified

Flat or Brewster or Specified

Flat,Spherical,Parallel and Wedged

Flat,Spherical,Parallel and Wedged

典型镀膜

Antireflective coating

 

Antireflective coating

Highreflective coating

Antireflective coating

 

Antireflective coating

 

 

 

 

7.被动晶体

Cr4+:YAG

物理特性

化学分子

Cr4+:Y3A15O12

晶体结构

Cubic Garnet

还原时间

8.5us

莫氏硬度

8.5

密度

4.56g/cm^3

晶向

[100]+/-10°

热导系数

12.13W/m/k

折射率

1.82@1064nm

 

光学性质

基态吸收截面

δs1=4.3*10-450px^2

发散状态的吸收截面

δs1=4.3*10-450px^2

荧光寿命

3.4us

能力

Cr4+参杂量

0.5mol%-3mol%

孔径

2*2-14*14mm

初始透过率

10%-99%

 

技术指标

尺寸公差

(W+/-0.1mm)*(H+/-0.1mm)*(L+0.2mm/-0.1mm)

面形

<λ/8@633nm

光洁度

Better than 10/5 Scratch /Dig per MIL-O-13830A

平行度

<20 arc seconds

垂直度

<5 arc minutes

透过波前

Less than λ/8@633nm

通光口径

>90% Central Area

镀膜

Anti-reflective

 

8.TGG单晶

TGG单晶是制作法拉第旋光器及隔离器的最佳磁光材料,法拉第旋光器由TGG晶棒和一个特殊设计的磁体组成。

通过磁光材料的光束的偏振方向将在磁场作用下发生偏转,其偏转方向只与磁场方向有关,而与光束传播方向无关

、。光隔离器由一个45度偏转的旋光器和一对偏振态成45度偏振器组成,它使光束仅能沿一个方向通过,而使反向

光束被阻隔。TGG单晶具有大的磁光常数、高热导性、低的光损失和高激光损伤阈值,广泛应用于YAG激光器、

掺钛宝石可调谐激光器和环型腔激光器中。

 

Crystal

Terbium Gallium Garnet(Tb3Ga5O12)

定向精度

[111]Within 5 Degrees

透过波前(每英寸长度)

λ/8

消光比

30Db over 2/3 Clear Aperture

直径

+0.000″/-0.002″

长度公差

+0.010/-0.010″

倒角

0.005″+/-0.003″@45°+/-5°

面形

λ/10 wave@633nm

平行度

<1 minutes of arc

侧面垂直度

<10 minutes of arc

光洁度

10/5Scratch /Dig per MIL-O-13830A

反射率

<0.25%@1064nm< p="">

热导吸收

7.4W cm-1K-1

折射率

1.95@1064nm

9.光学晶体

CaF2

CaF2 在170nm到7800nm是具有良好传输性能的晶体。它能溶于水,易受热冲击。CaF2广泛用于窗片,透镜,棱镜等。

l 透过范围:170nm-7800nm

l 热膨胀系数:18.85*10-6/K

l 密度:3.18g/cm^3

蓝宝石

蓝宝石是一种单晶氧化铝(氧化铝)。这是一个最坚硬的材料。蓝宝石具有良好的传输特性在可见光和近红外光谱。它具有

机械强度高、耐化学性能、热导率和热稳定性。它常被用作窗片材料在特定的领域如航天技术。

物理性能

Crystal Symmetry Heaxgonal

System

晶体常数

a=4.75;c=12.97

透明度范围

0.18-4.5um

密度

3.98g/cm^3

莫氏硬度

9

熔点

2030℃

热导系数

0.04W/m/k

热膨胀系数

8.4*10-6/k

折射率

1.755

Silicon(si) Crystals

硅(Si)是常用的作为衬底材料对红外ftx交易所新手教程和窗片,在1.5 um-8um。在9nm时强吸收也使得它不适合于CO2激光

传输的应用程序,但由于其高热电导率和低密度,它经常被用于激光镜。硅也是一个有用的发射机在20 um范围。

 

物理性能

材料类型

CZ FZ;N or P

晶体定向

{100}{111}

电阻率 (Ohm/cm)

0.003-50

热导系数(J/K.M.S)

163.3@273K

密度

2.33g/cm^3 at20℃

熔点

1410℃

沸点

3265℃

努氏硬度

1150

透光范围

1000nm-10000nm,30000nm-300000nm